ABSTRACT: High-performance and lightweight carbon aerogels (CAs) have attracted considerable attention in various fields such as electrochemistry, catalysis, adsorption, energy storage, and so on. However, finding an environmentally friendly and efficient preparation method and achieving a controllable performance of CAs are still a challenge. Herein, a series of anisotropic carbon/ graphene composite aerogels were synthesized by unidirectional freezing of polyamic acid ammonium salt/graphene oxide (PAS/ GO) suspension followed by lyophilization, thermal imidization, and carbonization. The prepared aerogels presented a tubular pore structure oriented along the freezing direction. The GO dispersed in the polymer matrix reinforced the skeleton of aerogels, which significantly inhibited the volume shrinkage during the preparation process, thus giving low densities of 0.074−0.185 g cm−3. In addition, the oriented pore structure endowed the composite aerogels with obviously anisotropic heat insulation performance. The radial thermal conductivity was as low as 0.038 W m−1 K−1 at the density of 0.074 g cm−3. When the initial content of GO rose to 20 phr, the resultant aerogels exhibited a high electrical conductivity of about 0.77 S cm−1 in the radial direction and the electromagnetic interference shielding effectiveness (EMI SE) reached 54.6 dB at the same time. Therefore, this study provided a facile and environmentally friendly method to prepare lightweight and anisotropic carbon aerogels. KEYWORDS: graphene oxide, polyimide, carbon aerogel, anisotropy, thermal insulation, electromagnetic interference shielding
947
- 湿法珠磨制备米诺地尔纳米颗粒实现高效靶向毛囊
- 硅碳负极助力锂离子电池能量密度提升
- 粒度、粒形分析技术助力3D打印材料发展
- 【Nat. Chem. Eng.】一维孔道中的动态分子口袋用于从C2-C4炔烃中分离乙烯
- 可见异物检查仪在提升药品质量与安全方面的作用
- CytoFLEX 流式细胞仪如何表征外泌体?
- 瓦楞原纸的边压强度(CCT)
- ATS干货分享丨高压均质法控制多糖结合疫苗多糖长度,优化疫苗免疫原性
- 压实度与密实度的区别
- 振实密度和压实密度的关系
- 勃姆石专用气流粉碎机分级机打散机
- 国产新品泡沫起升仪可替代德国format
- 国内首个他达拉非新剂型获批
- APS-100超声法粒度仪在ZnO纳米颗粒和ZnO-EG纳米流体方面的应用
- 气流筛分仪200lsn汇美科HMK-200始于2017
- 如何有效分析印刷品的抗擦性以及涂层硬度